Corrosion Behavior of Titanium Ti6Al4V ELI Bioceramic Coated Alloy in Artificial Saliva Modified Liquid at Fluctuating Temperatures Perilaku Korosi Paduan Titanium Ti6Al4V ELI Dilapisi Biokeramik pada Cairan Modifikasi Air Ludah Buatan pada Temperatur yang Berfluktuasi

Article Sidebar

Picture in here are illustration from public domain image or provided by the author, as part of their works
PDF XML EPUB
Published: Dec 7, 2021
DOI: https://doi.org/10.21070/r.e.m.v6i2.1627
Keywords:
Nano hydroxyapatite; Dental implants; Corrosion; Titanium Alloy; Temperature fluctuation

Main Article Content

Riza Muharni
Universitas Muhammadiyah Sumatera Barat
Aminar Sutra Dewi

Abstract

Titanium paduan merupakan material implan yang banyak digunakan untuk implan medis terutama bidang kedokteran gigi ( ortodentik ). Aplikasi implan gigi pada rongga mulut mengalami fluktuasi temperatur sesuai dengan temperatur makanan dan minuman yang masuk kedalam mulut sehingga membuat implan mudah terkorosi. Pada penelitian ini dilakukan pelapisan biokeramik hidroksiapatit pada permukaan Ti6Al4V ELI dengan metode EPD kemudian direndam dengan larutan air ludah buatan selama 6 minggu pada temperatur yang berfluktuasi yaitu 20ºC dan 60ºC. Tujuan dari penelitian ini adalah mengetahui pengaruh temperatur fluktuasi dalam air ludah buatan terhadap laju korosi dari Ti6Al4V ELI yang dilapisi biokeramik dengan metode weight loss ( kehilangan berat ) dan mengetahui pengaruh temperatur fluktuasi dalam air ludah buatan terhadap nilai kekerasan dari Ti6Al4V ELI yang dilapisi biokeramik.Hasilnya laju korosi menurun dari 1,10 mpy menjadi 0,43 mpy dan nilai kekerasan menurun dari 317 HVN menjadi  200 HVN. Hal ini menunjukkan bahwa hidroksiapatit dapat menghambat korosi tetapi tidak dapat mempertahankan sifat mekanis dari implan.

Article Details

Issue
Vol 6 No 2 (2021): December
Section
Articles

Copyright (c) 2021 riza muharni riza muharni

Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

Copyright Notice

Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution 4.0 International License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.

References

[1] Balgies et al, “Sintesis Dan Karakterisasi Hidroksiapatit Menggunakan Analisis X - Ray Diffraction,” Pros. Semin. Nas. Hamburan Neutron dan Sinar-X ke 8, pp. 10–13, 2011.
[2] R. Muharni, “Pelapisan Hidroksiapatit Nano dengan Metode Electro Phoretic Deposition pada Ti6Al4V ELI untuk Dental Implant R Muharni / Jurnal Rekayasa Mesin,” vol. 15, no. 3, pp. 207–211, 2020.
[3] B. I. Baddar et al, “Journal of Advanced Research in Fluid Hydroxyapatite and Thermal Oxidation as Intermediate Layer on Metallic Biomaterial for Medical Implant : A Review Keywords :,” vol. 1, no. 1, pp. 138–150, 2019.
[4] Suci et al, “CANGKANG KERANG ALE-ALE MENGGUNAKAN METODE PRESIPITASI DOUBLE STIRRING,” vol. 8, pp. 73–81, 2020.
[5] Desmarita Leni D et al, “ISSN 2599-2081 EISSN 2599-2090 Fak . Teknik UMSB Rang Teknik Journal,” Rang Tek. J., vol. I, no. 1, pp. 27–33, 2018.
[6] C. Yulian, “Biokompatibilitas Material Titanium Implan Gigi,” IDJ, vol. 8, no. November, pp. 53–58, 2019.
[7] D. P. Utami et al, “Laporan penelitian Peran metode modifikasi permukaan implan terhadap keberhasilan osseointegrasi,” pp. 95–101, 2019, doi: 10.24198/jkg.v31i2.17967.
[8] S. Anderson et al, “Corrosion Characteristics Of Titanium TNTZ And Ti-6Al-4V ELI In Artificial Saliva Solution At Human Body Temperature,” no. 04, pp. 240–245, 2021.
[9] H. Farnoush et al, “An innovative fabrication of nano-HA coatings on Ti-CaP nanocomposite layer using a combination of friction stir processing and electrophoretic deposition,” Ceram. Int., vol. 39, no. 2, pp. 1477–1483, Mar. 2013, doi: 10.1016/J.CERAMINT.2012.07.092.
[10] J. Affi et al, “Corrosion Behavior of New Type Titanium Alloy As Candidate for Dental Wires in Artificial Saliva on Fluctuating Temperatures,” IOP Conf. Ser. Mater. Sci. Eng., vol. 547, no. 1, pp. 1–9, 2019, doi: 10.1088/1757-899X/547/1/012022.
[11] S. Cabanas-polo et al, “applications,” J. Eur. Ceram. Soc., 2015, doi: 10.1016/j.jeurceramsoc.2015.05.030.
[12] J. Affi et al., “PELAPISAN HIDROKSIAPATIT PADA PADUAN TITANIUM DENGAN ELECTROPHORETIC DEPOSITION ( EPD ) UNTUK IMPLAN ORTOPEDI,” pp. 9–10, 2019.
[13] L. JIN et al, “Effects of surface nanocrystallization on corrosion resistance of β-type titanium alloy,” Trans. Nonferrous Met. Soc. China, vol. 24, no. 8, pp. 2529–2535, Aug. 2014, doi: 10.1016/S1003-6326(14)63379-3.
[14] H. Fajri et al,“Corrosion Behaviour of Collagen Coated and Uncoated Biomedical Titanium Alloy (TNTZ) Within Human Synovial Fluid Corrosion Behaviour of Collagen Coated and Uncoated Biomedical Titanium Alloy ( TNTZ ) Within Human Synovial Fluid,” 2019, doi: 10.1088/1757-899X/547/1/012007.
[15] R. Muharni et al, “Corrosion behavior of Ti6Al4V ELI coated by bioceramic HA in artificial saliva at fluctuating temperatures,” IOP Conf. Ser. Mater. Sci. Eng., vol. 602, no. 1, 2019, doi: 10.1088/1757-899X/602/1/012090.