Pengaruh Flux Elektroda AWS 5.1 E 6013 Dicelup Oli pada Pengelasan Besi Cor Kelabu FC-25 Terhadap Kekuatan Tarik
Effect of Oil Dipped AWS 5.1 E 6013 Electrode Flux on FC-25 Gray Cast Iron Welding on Tensile Strength
Abstract
In this study using specimens of gray cast iron Fc-25 (grade 2500). The test specimen is needed there 12 specimens include three test specimen material (base metal), 3 specimen variety of welding electrodes cast CI-A1, 3 specimen variety of welding using welding electrodes AWS 5.1 E6013 without immersion oil, three specimens variation welding using welding electrodes 5.1 AWS E6013 with immersion oil. The results of testing specimens welding electrodes cast CI-A1 in the amount of 16.63 MPa with 0.84% strain and a variety of welding electrode AWS E6013 5.1 with immersion oil also has the highest ultimate tensile strength of welding another variation in the amount of 17.98 MPa with a strain of 0.48% , While the lowest was tensile strength using a variety of welding electrode AWS E6013 5.1 without immersion oil that is 16.28 MPa with a strain of 0.49%.
References
Mulyadi, dkk., “Rekayasa Elektroda Mild Steel (LB-52) dicelup Olie Sebagai Pengganti Alternatif Elektroda Besi Cor (CIA-1) Pada Pengelasan Besi Cor Kelabu Fc-30 Di Lihat Dari Segi Kekuatan Tarik Hasil Pengelasan,” Prosiding SNFT, Vol 5. Hal: 52-61, 2015.
Khusnul Yaqin, Muhammad dkk, “Pengaruh Preheat Dan Postheat Terhadap Lebar Haz, Strukturmikro, Dan Distribusi Kekerasan Pada Proses Pengelasan Smaw Besi Cor Kelabu Fc 25”, Jurnal Teknik Material Dan Metalurgi, Institut Teknologi Sepuluh Nopember Surabaya, 2011.
Callister, William D, Materials Science and Engineering, John Willey &Sons, Inc. USA., 2011.
Wiryosumarto, Harsono dan Okumura, Toshie, Teknologi Pengelasan Logam, Edisi Cet. Ke-8, PT Pradnya Paramita, Jakarta, 2000.
Widharto, Sri, Petunjuk Kerja Las, Edisi Cet. Ke-5, PT Pradnya Paramita, Jakarta, 2003.
Copyright (c) 2018 Aris Hermanto, Iswanto Iswanto
This work is licensed under a Creative Commons Attribution 4.0 International License.
Copyright Notice
Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution 4.0 International License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.